Pengaruh Orientasi Sudut Anyam Lamina Pada Fiberglass Terhadap Kekuatan Tarik Komposit Matriks Polyester

Risal Risal, Sudarsono Sudarsono, Abd. Kadir

Abstract


The purpose of this research is to find the tensile strength of fiberglass composite against the orientation of the lamina weaving angle. In this research composite making uses a hand lay-up method, with a fiber-matrix fraction of 30 % : 70 %. Specimen were made with ASTM D 638-01 tensile test standar. The result showed that the highes tensile test specimen value with the orientation of the weaving lamina angel is 0o/90o, 0o/90o, 0o/90o, 0o/90o, 0o/90o, 0o/90o, 0o/90o, 0o/90o which is 135,568 N/mm2. While the lowest tensile test specimen value are in the orientation of the weaving angles of lamina 0o/90o, 15o/105o, 30o/120o, -15o/-105o, -15o/-105o, 30o/120o, 15o/105o, 0o/90o, with voltage values tensile strength of 106,447 N/mm2.

 Keywors: Composite, fiberglass, angle orientation, tensile trength.


Full Text:

PDF

Refbacks

  • There are currently no refbacks.


Penanggung Jawab: Dekan Fakultas Teknik Universitas Halu Oleo

Pimpinan Redaksi: Aminur, ST., M.Eng

Mitra Bestari: DR. Akhyar, S.T., M.Eng.
Jurusan Teknik Mesin, Fakultas Teknik, Universitas Syiah Kuala, Banda Aceh 

Dr. Muhammad Syukron, S.T.,M.Eng. 
Jurusan Teknik Mesin, FakultasTeknik, Universitas Muhammadiyah, Surakarta

Dr. Eng. Sudarsono, S.T.,M.Eng. 
Jurusan Teknik Mesin, FakultasTeknik, Universitas Halu Oleo, Kendari

Dr. Eng. Lukas Kano Mangalla, S.T.,M.T. 
Jurusan Teknik Mesin, FakultasTeknik, Universitas Halu Oleo, Kendari

Dr. Eng. Nanang Endriatno, S.T.,M.T. 
Jurusan Teknik Mesin, FakultasTeknik, Universitas Halu Oleo, Kendari

Dewan Editor: Ir. H. Ridway Balaka,M.Eng.
Ir. Salimin, M.T.
Muhammad Hasbi, ST., M.T.
Budiman Sudia, S.T., M.T
Jenny Delly, S.T., M.T. 
La Hasanudin, S.S.T., M.T.
Raden Rinova Sisworo, S.T., M.Eng.
Prinob Aksar, S.T, M.T.

Penerbit: Jurusan Teknik Mesin Fakultas Teknik  

Universitas Halu Oleo
Kampus Hijau Bumi Tri Dharma Jl. HEA. Mokodompit
Anduonohu Telp.(0401)3194347.
e-mail : jurnal.enthalpy.uho@gmail.com

e-ISSN: 2502-8944